Fused Materials 3D Filaments
1.75/2.85mm| Filament | Print Temp (°C) | Bed Temp (°C) | Distortion Temp (°C) | Density (g/cm³) | Melt Flow Index (g/10min) | Tensile Strength (MPa) | Elongation at Break (%) | Bending Stength (MPa) | IZOD Impact Strength (kJ/m²) |
|---|
Filament | Print Temp (°C) | Bed Temp (°C) | Distortion Temp (°C) | Density (g/cm³) | Melt Flow Index (g/10min) | Tensile Strength (MPa) | Elongation at Break (%) | Bending Stength (MPa) | IZOD Impact Strength (kJ/m²) |
|---|---|---|---|---|---|---|---|---|---|
| ABS | 230-260 | 80-100 | 88 | 1.05 g/cm³ | 1.6 g/10min | 54 MPa | 20% | 77.5 MPa | 19 kJ/m² |
| ASA | 200-250 | 80-100 | 87 | 1.05 g/cm³ | 11 g/10min | 46 MPa | 60% | 83.4 MPa | 20 kJ/m³ |
| PA12 | 230-250 | 90-110 | 92 | 1.04 g/cm³ | 8.91 g/10min | 70.0 MPa | 50% | 110.5 MPa | 3.5 kJ/m² |
| PC+ | 235-260 | 100-120 | 99 | 1.28 g/cm³ | 10 g/10min | 61.8 MPa | 110% | 90.2 MPa | 80 kJ/m² |
| PETG | 200-240 | 75-85 | 70 | 1.27 g/cm³ | 1.2 g/10min | 53.0 MPa | 70% | 2150 MPa | 90 J/m |
| PLA | 190-230 | 60-80 | 70 | 1.20-1.30 g/cm³ | 2.0-10 g/10min | >5.0 MPa | >3.0% | 60 MPa | 3.0-5.0 kJ/m² |
| PVA | 190-220 | 0 | 85 | 1.25 g/cm³ | 1.5-2.0 g/10min | 11 MPa | 11% | None | None |
| TPU | 220-240 | 75-85 | 110 | 1.21 g/cm³ | 2.0-3.0 g/10min | 40.0 MPa | 550% | None | None |
| Cleaning Filament | 160-300 | - | 45 | 0.95 g/cm³ | - | 23 MPa | 580% | - | 29 kJ/m² |
Showing 1 to 9 of 9 entries